dc.identifier.citationGomez Ortega, J. A. (2012). Study of polymer flow behavior in cavity filling of alignment structures in micro hot embossing (Unpublished thesis). Texas State University-San Marcos, San Marcos, Texas.
dc.identifier.urihttps://digital.library.txstate.edu/handle/10877/4258
dc.description.abstract

The behavior of polymer flow is a critical aspect in micro hot embossing. The flow behavior significantly depends on the process parameters including molding temperatures and displacement of a mold with respect to a polymer substrate. To achieve accurate replication of microstructures, it is necessary to predict the flow behavior depending on the process parameters.

Two alignment structures were chosen as embossing features to demonstrate the flow behavior of polymer in hot embossing. The post has a height of 925 µm and a radius of 500 µm. Polymethyl-Methacrylate (PMMA) was selected as a substrate material. Computer-aided engineering models (CAE), using DEFORM 2D (SFTC, Columbus, OH), were used to simulate the flow behavior in the filling of a hemisphere-tipped cavity in molding. Simulations were performed to help understand the flow behavior of the polymer while varying the molding temperatures and the displacement of the mold. The simulation conditions were mold temperatures of 75, 100, 125, and 150˚C, displacement of mold of 0.5, 1.0 2.0, 2.5 mm, and speed of embossing 0.008 mm/sec.

Replication fidelity of the post was evaluated using the height of molded hemisphere-tipped post. The height of the molded post increases while the molding temperature and displacement increase. Incomplete filling of polymer at the cavity was observed at molding temperature of 75°C when the displacement increased from 0.5 mm to 2.5 mm. As molding temperature increased to 125°C, the cavity was completely filled at the displacement of 1.5, 2.0, and 2.5 mm. The increase of mold temperature yielded better cavity filling because the higher molding temperature decreased the fluidic resistance of the polymer. It can be explained by a glass transition temperature of PMMA, about 105°C, so PMMA significantly softens above this temperature.

Numerical simulation predicted the flow behavior of polymer in micro hot embossing of the alignment structure. These results can be used to determine proper process parameters for the microfabrication of polymer microstructures.

dc.formatText
dc.format.extent84 pages
dc.format.medium1 file (.pdf)
dc.language.isoen
dc.subjectHot embossing
dc.subjectPolyer
dc.subjectPMMA
dc.subjectCavity filling
dc.subjectMicrostructures
dc.subjectSimulation
dc.subjectNumerical analysis
dc.subject.lcshMicrofabricationen_US
dc.subject.lcshMaterials at high temperaturesen_US
dc.subject.lcshLiquid filmsen_US
dc.subject.lcshMicrotechnologyen_US
dc.titleStudy of Polymer Flow Behavior in Cavity Filling of Alignment Structures in Micro Hot Embossing
txstate.documenttypeThesis
dc.contributor.committeeMemberKim, Yoo Jae
dc.contributor.committeeMemberSong, In-Hyouk
thesis.degree.departmentEngineering Technology
thesis.degree.disciplineIndustrial Technology
thesis.degree.grantorTexas State University-San Marcos
thesis.degree.levelMasters
thesis.degree.nameMaster of Science
dc.description.departmentEngineering Technology


Download

Thumbnail

This item appears in the following Collection(s)

Show simple item record