Thermoelectric Property Study of N-Type PbTe
dc.contributor.advisor | Droopad, Ravindranath | |
dc.contributor.author | Garza, Rico Z. | |
dc.contributor.committeeMember | Geerts, Wilhelmus J. | |
dc.contributor.committeeMember | Zirkle, Tom | |
dc.date.accessioned | 2014-04-15T19:17:08Z | |
dc.date.available | 2014-04-15T19:17:08Z | |
dc.date.issued | 2014-05 | |
dc.description.abstract | In this study, the thermoelectric power density of In-doped PbTe wafers were measured and compared to I-doped PbTe wafers. Both I-doped and In-doped PbTe ingots were grown using a modified vertical Bridgman technique. The crystals were grown in the n-type region of the phase diagram. The I-doped PbTe was doped in order to obtain an electron concentration of 3x10(19)cm(-3) and the In-doped PbTe was doped at 0.1 at.%. The I-doped PbTe possesses a thermoelectric power density of ~30 W/cm2 whereas the In-doped PbTe has a power density of ~15 W/cm2. Despite the In-doped PbTe having a potential almost two times that of the I-doped PbTe, I-doped PbTe possesses a higher initial ZT in the temperature range of 50-450°C along with a normalized power output of almost two times that of the indium doped samples. It is therefore concluded that the use of I-doped PbTe in thermoelectric devices would be greatly preferred over In-doped PbTe from a commercial standpoint. | |
dc.description.department | Physics | |
dc.format | Text | |
dc.format.extent | 68 pages | |
dc.format.medium | 1 file (.pdf) | |
dc.identifier.citation | Garza, R. Z. (2014). Thermoelectric property study of N-type PbTe (Unpublished thesis). Texas State University, San Marcos, Texas. | |
dc.identifier.uri | https://hdl.handle.net/10877/4965 | |
dc.language.iso | en | |
dc.subject | Thermoelectrics, PbTe | |
dc.subject | PbTe | |
dc.title | Thermoelectric Property Study of N-Type PbTe | |
dc.type | Thesis | |
thesis.degree.department | Physics | |
thesis.degree.discipline | Physics | |
thesis.degree.grantor | Texas State University | |
thesis.degree.level | Masters | |
thesis.degree.name | Master of Science |